Preparação de heteroestruturas formadas por hidróxidos duplos lamelares recobertos com sílica mesoporosa

Página do item simplificado
dc.contributor.advisorBizeto, Marcos Augusto [UNIFESP]
dc.contributor.advisor-coConstantino, Vera Regina Leopoldo
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/3087447388007700pt_BR
dc.contributor.advisorLatteshttp://lattes.cnpq.br/8149318154113564pt_BR
dc.contributor.authorBianconi, Lister Pronestino [UNIFESP]
dc.contributor.authorLatteshttp://lattes.cnpq.br/6694663714265223pt_BR
dc.coverage.spatialDiademapt_BR
dc.date.accessioned2020-07-22T18:57:28Z
dc.date.available2020-07-22T18:57:28Z
dc.date.issued2019
dc.description.abstractSólidos inorgânicos porosos são materiais que apresentam grande área superficial e são normalmente utilizados em aplicações envolvidas com separação, adsorção, catálise e liberação modificada de substâncias, que são processos que se beneficiam de tal propriedade. Os hidróxidos duplos lamelares (HDL) e as sílicas mesoporosas (SM) são exemplos de sólidos inorgânicos porosos que despertam muito interesse científico e tecnológico, não só pela grande área superficial que possuem, mas devido as suas propriedades estruturais, texturais e químicas. Neste estudo, os HDL do tipo hidrotalcita [Mg4Al2(OH)12]CO3·xH2O e [Zn4Al2(OH)12]CO3·xH2O foram combinados à SM visando produzir heteroestruturas compostas de um núcleo de HDL envolto por uma camada externa de SM. Diferentes condições sintéticas foram testadas visando produzir um recobrimento de sílica uniforme e com porosidade ordenada, mas utilizando quantidades menores de direcionador estrutural usado para formação dos poros na sílica em relação aos métodos reportados na literatura, além do uso do HDL com Zn na composição, ainda não reportado na literatura. A difratometria de raios X e a espectroscopia vibracional confirmaram a presença das fases de sílica e HDL. A distribuição e o arranjo entre essas fases foram determinados por microscopias eletrônicas de varredura e transmissão. A microscopia de varredura mostrou uma grande influência da razão molar entre os reagentes e dos reagentes utilizados na etapa do recobrimento no hábito da partícula resultante. A microscopia de transmissão indicou que o recobrimento das partículas de HDL foi efetivo quando usado menores concentrações de direcionador estrutural e sem etanol como cosolvente, aparentemente, uniforme e sem a formação de fases segregadas. Entretanto, o processo de calcinação para remoção do molde levou à desestruturação do HDL, fato que não ocorreu quando o molde foi removido por extração. A reconstrução parcial do arranjo lamelar do HDL na heteroestrutura calcinada foi conseguida através do efeito memória, que algumas das fases HDL apresentam. A calcinação também afetou a porosidade das heteroestruturas, que somadas ao efeito de reconstrução parcial da fase de HDL observado, podem indicar a ocorrência de uma possível reação entre a sílica e o HDL, formando uma outra fase não porosa, fato que ainda precisa ser investigado em estudos futuros. Os resultados mais importantes deste estudo foram: o desenvolvimento de um procedimento sintético que utilizou menor concentração do direcionador estrutural, que possibilitou a remoção posterior por extração de forma mais eficiente; a confecção de heteroestruturas inéditas com o HDL Zn2Al-CO3; a avaliação do efeito memória para reconstrução da estrutura lamelar do HDL na heteroestrutura após o processo de calcinação para remoção do direcionador estrutural usado na formação do recobrimento de sílica.pt_BR
dc.description.abstractInorganic porous solids are materials with large surface area, commonly used in applications such as separation, adsorption, catalysis and modified release of substances, which are processes benefited from such property. Layered double hydroxides (LDH) and mesoporous silica (MS) are examples of inorganic solids that have such characteristics and are currently of great scientific and technological interest not only for their large surface area but also for their structural, textural and chemical properties. In this study, the hydrotalcite-like LDH [Mg4Al2(OH)12]CO3•xH2O and [Zn4Al2(OH)12]CO3•xH+O were combined to MS to produce heterostructures composed of an LDH core surrounded by an MS shell (MII 2Al-CO3@mSiO2). Different synthetic conditions were tested in order to obtain a uniform and ordered porous silica coating but using smaller amounts of structural directing agent compared to the methods reported in the literature, besides the use of the Zn2Al-CO3 LDH not yet already reported in the literature. X-ray diffraction and vibrational spectroscopy confirmed the presence of silica and LDH phases in the produced heterostructures. The distribution and arrangement between these phases were determined by scanning and transmission electron microscopy. Scanning microscopy showed a great influence of molar composition among the reagents used in the coating step in the habit of the resulting particle. Transmission microscopy indicated that the LDH particle coating was effective and apparently uniform without the formation of segregated phases. However, the calcination process for template removal led to the destruction of the LDH, which did not occur when the template was removed by extraction. Partial reconstruction of the lamellar arrangement of LDH after calcination was achieved through the memory effect. Calcination also affected the porosity of the heterostructures, which in addition to the partial reconstruction effect of the observed LDH phase, could indicate the occurrence of a possible reaction between silica and LDH, forming another non-porous phase, a fact that has must be investigated in future studies. The most important results of this study were: the development of a synthetic procedure that used a lower concentration of the structural directing agent; the production of heterostructures containing Zn2Al-CO3 as the core; the evaluation of the memory effect to reconstruction the LDH core after calcination to remove the template.en
dc.description.provenanceSubmitted by Argélia Peixoto (argeliapeixoto@gmail.com) on 2020-07-21T20:30:35Z No. of bitstreams: 1 Dissertação - Lister Pronestino Bianconi.pdf: 4618040 bytes, checksum: 483d71a78541faf4a43aedec3d7632b7 (MD5)en
dc.description.provenanceApproved for entry into archive by Argelia Peixoto (argelia.peixoto@unifesp.br) on 2020-07-22T18:57:28Z (GMT) No. of bitstreams: 1 Dissertação - Lister Pronestino Bianconi.pdf: 4618040 bytes, checksum: 483d71a78541faf4a43aedec3d7632b7 (MD5)en
dc.description.provenanceMade available in DSpace on 2020-07-22T18:57:28Z (GMT). No. of bitstreams: 1 Dissertação - Lister Pronestino Bianconi.pdf: 4618040 bytes, checksum: 483d71a78541faf4a43aedec3d7632b7 (MD5) Previous issue date: 2019en
dc.description.sponsorshipFundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)pt_BR
dc.description.sponsorshipIDCAPES: 1744920pt_BR
dc.description.sponsorshipIDFAPESP: 2016/50317-9pt_BR
dc.description.sponsorshipIDFAPESP: 2019/05467-0.pt_BR
dc.format.extent75 f.pt_BR
dc.identifier.urihttps://repositorio.unifesp.br/handle/11600/56211
dc.languageporpt_BR
dc.publisherUniversidade Federal de São Paulopt_BR
dc.rightsAcesso abertopt_BR
dc.subjectHidróxidos duplos lamelarespt_BR
dc.subjectSílica mesoporosapt_BR
dc.subjectHeteroestruturaspt_BR
dc.subjectCore-shellpt_BR
dc.subjectEfeito memóriapt_BR
dc.subjectLayered double hydroxidesen
dc.subjectMesoporous silicaen
dc.subjectHeterostructuresen
dc.subjectCoreshellen
dc.subjectMemory effecten
dc.titlePreparação de heteroestruturas formadas por hidróxidos duplos lamelares recobertos com sílica mesoporosapt_BR
dc.typeDissertação de mestradopt_BR
unifesp.assessoresproreitoriasNão se aplicapt_BR
unifesp.campusInstituto de Ciências Ambientais, Químicas e Farmacêuticas (ICAQF)pt_BR
unifesp.departamentoNão se aplicapt_BR
unifesp.especializacaoNão se aplicapt_BR
unifesp.graduacaoNão se aplicapt_BR
unifesp.graduateProgramCiência e Tecnologia da Sustentabilidadept_BR
unifesp.knowledgeAreaCiências da sustentabilidadept_BR
unifesp.researchAreaDesenvolvimento e Aplicações de Materiais Sustentáveispt_BR
Arquivos
Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
Dissertação - Lister Pronestino Bianconi.pdf
Tamanho:
4.4 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
license.txt
Tamanho:
5.35 KB
Formato:
Item-specific license agreed upon to submission
Descrição:
Baixar
Coleções
PPG - Química - Ciência e Tecnologia da Sustentabilidade