Desenvolvimento de compósitos de PCL e pó de madeira

Página do item simplificado
dc.contributor.advisorMontagna, Larissa Stieven
dc.contributor.advisor-coPassador, Fábio Roberto
dc.contributor.advisor-coLatteshttp://lattes.cnpq.br/0152213852695153pt_BR
dc.contributor.advisorLatteshttp://lattes.cnpq.br/6872952353977748pt_BR
dc.contributor.authorCintra, Sheila Cristina [UNIFESP]
dc.contributor.authorLatteshttp://lattes.cnpq.br/6041647409792564pt_BR
dc.coverage.spatialSão José dos Campospt_BR
dc.date.accessioned2021-03-25T20:10:06Z
dc.date.available2021-03-25T20:10:06Z
dc.date.issued2019-11-20
dc.description.abstractMateriais poliméricos são bastante utilizados em diversos setores devido à sua alta resistência à degradação. A maioria dos polímeros, contudo, são provenientes de fontes não renováveis e podem comprometer o meio ambiente caso seja feito um descarte inadequado. Visando diminuir os impactos ambientais, o presente Trabalho de Conclusão de Curso propôs o desenvolvimento de compósitos a partir de policaprolactona (PCL), um polímero biodegradável, reforçado com pó de madeira (PM) com teores de 0, 5 e 15% em massa dessa carga natural. Os corpos de prova foram obtidos por meio de uma extrusora de dupla rosca, seguido por prensagem à quente. Foram realizados ensaios de absorção de água, ângulo de contato, envelhecimento em estufa, resistência ao impacto Izod, dureza Shore D e resistência à tração uniaxial. Por fim, foram feitas análises de microscopia eletrônica de varredura (MEV) e calorimetria exploratória diferencial (DSC). Pelos resultados encontrados, notou-se que é possível desenvolver compósitos a base de PCL e pó madeira como reforço, sem nenhum tratamento superficial a partir de uma extrusora, apresentando grande potencial para substituir polímeros de fontes não renováveis. Observou-se que a presença do reforço contribui na degradação por hidrólise devido ao seu caráter hidrofílico. Conforme o aumento no teor de PM, principalmente para o PCL/15% PM, o material se tornou mais rígido devido ao aumento do módulo elástico correspondente a 61% em relação ao PCL puro. Ao analisar a morfologia dos corpos de prova, os compósitos de PCL com de PM apresentaram, de maneira geral, boa adesão interfacial com a matriz polimérica. Por sua vez, o compósito de PCL com adição de 5% em massa de PM apresentou resultados bastante satisfatórios em relação às propriedades mecânicas e térmicas, com uma boa interação com a matriz de PCL.pt_BR
dc.description.abstractPolymers are widely used in various sectors due to their high resistance to degradation. Such polymers, however, are from non-renewable sources and can be environmentally harmful if it is made improper disposal. In order to reduce the environmental impacts, the present work propose the development of composites based on polycaprolactone (PCL), a biodegradable polymer, reinforced with wood powder (WP) with 0, 5 and 15 wt%. The specimens were extruded followed by hot pressing. Water absorption, contact angle, greenhouse aging tests was performed such as Izod impact tests, Shore D hardness, and tensile test. Finally, the analysis of SEM and DSC were carried out. From the results, it is possible to develop composites based on the mixture of PCL and wood powder as natural filler without any surface treatment using an extruder while being capable to achieve the great potential for replacement of polymers from non-renewable sources. It was noticed that the presence of natural filler contributes to degradation by hydrolysis due to its hydrophilic character. As the WP content increases, specially for PCL/15% WP, the samples becomes more rigid due to the elastic modulus increase corresponding to 61% in comparison with the pure PCL. In general, good interfacial adhesion between the polymeric matrix and wood powder was observed. In turn, the PCL/WP composite with the addition of 5 wt% WP presented satisfactory results regarding the mechanical and thermal properties with good interaction between WP and PCL matrix.pt_BR
dc.description.sponsorshipNão recebi financiamentopt_BR
dc.format.extent52 f.pt_BR
dc.identifier.urihttps://repositorio.unifesp.br/handle/11600/60753
dc.languageporpt_BR
dc.publisherUniversidade Federal de São Paulopt_BR
dc.rightsinfo:eu-repo/semantics/openAccesspt_BR
dc.subjectpolicaprolactonapt_BR
dc.subjectpó de madeirapt_BR
dc.subjectcompósitospt_BR
dc.subjectpolímeros biodegradáveispt_BR
dc.titleDesenvolvimento de compósitos de PCL e pó de madeirapt_BR
dc.title.alternativeDevelopment of PCL/wood powder compositespt_BR
dc.typeinfo:eu-repo/semantics/bachelorThesispt_BR
unifesp.assessoresproreitoriasNão se aplicapt_BR
unifesp.campusInstituto de Ciência e Tecnologia (ICT)pt_BR
unifesp.departamentoNão se aplicapt_BR
unifesp.especializacaoNão se aplicapt_BR
unifesp.graduacaoEngenharia de Materiaispt_BR
unifesp.graduateProgramNão se aplicapt_BR
unifesp.knowledgeAreaOutrapt_BR
Arquivos
Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
TCC-Sheila Cristina Cintra.pdf
Tamanho:
2.48 MB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Licença do Pacote
Agora exibindo 1 - 3 de 3
Imagem de Miniatura
Nome:
license.txt
Tamanho:
5.3 KB
Formato:
Item-specific license agreed upon to submission
Descrição:
Baixar
Imagem de Miniatura
Nome:
Sheila Cintra -Termo Autorização.pdf
Tamanho:
142.95 KB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Imagem de Miniatura
Nome:
Termo_de_Responsabilidade_e_Autencidade_TCC_Unifesp_Portaria_Prograd._n._3-2021.pdf
Tamanho:
388.74 KB
Formato:
Adobe Portable Document Format
Descrição:
Baixar
Coleções
Engenharia de Materiais