    Desenvolvimento de compósitos de PCL e pó de madeira
    (Universidade Federal de São Paulo, 2019-11-20) Cintra, Sheila Cristina [UNIFESP]; Montagna, Larissa Stieven; Passador, Fábio Roberto; http://lattes.cnpq.br/0152213852695153; http://lattes.cnpq.br/6872952353977748; http://lattes.cnpq.br/6041647409792564
    Materiais poliméricos são bastante utilizados em diversos setores devido à sua alta resistência à degradação. A maioria dos polímeros, contudo, são provenientes de fontes não renováveis e podem comprometer o meio ambiente caso seja feito um descarte inadequado. Visando diminuir os impactos ambientais, o presente Trabalho de Conclusão de Curso propôs o desenvolvimento de compósitos a partir de policaprolactona (PCL), um polímero biodegradável, reforçado com pó de madeira (PM) com teores de 0, 5 e 15% em massa dessa carga natural. Os corpos de prova foram obtidos por meio de uma extrusora de dupla rosca, seguido por prensagem à quente. Foram realizados ensaios de absorção de água, ângulo de contato, envelhecimento em estufa, resistência ao impacto Izod, dureza Shore D e resistência à tração uniaxial. Por fim, foram feitas análises de microscopia eletrônica de varredura (MEV) e calorimetria exploratória diferencial (DSC). Pelos resultados encontrados, notou-se que é possível desenvolver compósitos a base de PCL e pó madeira como reforço, sem nenhum tratamento superficial a partir de uma extrusora, apresentando grande potencial para substituir polímeros de fontes não renováveis. Observou-se que a presença do reforço contribui na degradação por hidrólise devido ao seu caráter hidrofílico. Conforme o aumento no teor de PM, principalmente para o PCL/15% PM, o material se tornou mais rígido devido ao aumento do módulo elástico correspondente a 61% em relação ao PCL puro. Ao analisar a morfologia dos corpos de prova, os compósitos de PCL com de PM apresentaram, de maneira geral, boa adesão interfacial com a matriz polimérica. Por sua vez, o compósito de PCL com adição de 5% em massa de PM apresentou resultados bastante satisfatórios em relação às propriedades mecânicas e térmicas, com uma boa interação com a matriz de PCL.
  • Nenhuma Miniatura disponível
    Item
    Somente Metadadados
    Eletrofiação e caracterização dos compósitos de pla/-tcp e pcl/-tcp visando aplicações na engenharia tecidual
    (Universidade Federal de São Paulo (UNIFESP), 2015-01-29) Siqueira, Lilian de [UNIFESP]; Triches, Eliandra de Sousa Triches [UNIFESP]; Universidade Federal de São Paulo (UNIFESP)
    Studies related to poly (lactic acid) (PLA) and polycaprolactone (PCL) as a biomaterial have been widespread in recent decades. These polymers are characterized by its form of degradation and biocompatibility. However, they have some limitations such as the lack of bioactivity, hydrophobic surface and degradation in long term in vivo. These limitations can be apprimorated by incorporating inorganic fillers in the polymer matrix. Beta-tricalcium phosphate (?-TCP) has been recognized as an attractive biomaterial due to their similar chemical composition to the mineral component of bone. Moreover, it is bioactive, biodegradable and osteoinductive. This work aimed to produce and characterize porous mats composed of PLA/?-TCP and PCL/?-TCP composites by electrospinning. This is a simple and versatile method, and promotes the production of porous mats in micro and nano scale with great potential to applications in tissue engineering, mainly in bone regeneration. In order to do so, ?-TCP particles were synthesized by solid state reaction and different concentrations (1, 5 and 8 wt-%) were incorporated into the polymers matrices. The PLA/?-TCP and PCL/?-TCP mats were obtained by electrospinning. The samples were characterized by scanning electron microscopy (SEM), infrared spectroscopy (FTIR), differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA). Cell viability assays (MTT) were also performed. The mats presented porous, fibrous and interconnected structure. A wide range of average fiber diameter was observed for both polymers. The average diameter of the fibers varied in the range of 260 ± 51 to 546 ± 136 nm for the PLA and PLA/?-TCP mats and 640 ± 20 to 867 ± 40 nm for PCL and PCL/?-TCP mats. The presence of ?-TCP particles promoted changes in the mat?s degree of crystallinity. PLA/?-TCP and PCL/?-TCP mats exhibited biocompatibility showing up non cytotoxic as well as promoted a favorable inviroments. Simulated body fluid (SBF) results showed that PCL and PCL/?-TCP composite mats containing higher contents of ?-TCP presented a homogeneous apatite layer deposited on their surfaces.
  • Imagem de Miniatura
    Item
    Acesso aberto (Open Access)
    Síntese de poli(acrilato de hidroxietil caprolactona-co-metacrilato de metila)-g-pululana via polimerização em emulsão para produção de polímeros biodegradáveis
    (Universidade Federal de São Paulo, 2024-05-17) Santos, Samuel Augusto dos [UNIFESP]; Oliveira, Maurício Pinheiro de [UNIFESP]; http://lattes.cnpq.br/9091349305586921; http://lattes.cnpq.br/3912276542232842
    A síntese de copolímeros biodegradáveis em meio disperso, a partir de macromonômeros de ɛ-caprolactona e seus derivados é atraente em função da biocompatibilidade, biodegradabilidade e por apresentarem propriedades térmicas e mecânicas importantes para aplicações no segmento agroindustrial. Diante disso, copolímeros de poli(acrilato de hidroxietil caprolactona-co-metacrilato de metila)-g-pululana (poli(HECLA-co-MAM)-g-Pull) foram desenvolvidos por meio da técnica de polimerização em emulsão por semente in situ para obtenção de nanopartículas poliméricas (NPs) em dispersão aquosa e degradáveis. Inicialmente, foi determinado o tempo ótimo de hidrólise da Pull (redução da massa molar) em meio ácido para posterior estabilização das NPs. Na segunda etapa, foi estudado o efeito da concentração dos monômeros de HECLA e MAM, na presença da Pull como estabilizante polimérico, visando encontrar a melhor relação monomérica e as melhores condições de processo para obter NPs estáveis. Os látexes e os copolímeros foram avaliados em relação à conversão global, propriedades coloidais (diâmetro de partícula, tensão superficial, pH, potencial zeta, estabilidade coloidal), ângulo de contato, absorção de água, propriedades térmicas e propriedades mecânicas. Os resultados obtidos comprovaram que foi possível obter látexes de poli(HECLA-co-MAM)-g-Pull, onde o tempo de hidrólise ótimo da Pull foi igual a 30 min para obtenção de látexes estáveis. Além disso, foi verificado que o aumento da fração monomérica de HECLA resultou em látexes com menor estabilidade coloidal, sendo necessário o ajuste do pH para manter as NPs estáveis (látex Pull-30-H100). No estudo de degradação dos polímeros via úmida foi verificado que a degradação máxima do copolímero foi igual a 55 % e que a biodegração foi dependente da concentração de HECLA utilizada. Por fim, foi comprovada a degradação dos filmes poliméricos (Pull-30-H90, Pull-30-H95 e Pull-30-H100) em solo agrícola para diferentes tempos de ação dos microrganismos nos filmes poliméricos. Portanto, foi possível desenvolver NPs estáveis e polímeros biodegradáveis a partir da técnica de polimerização em emulsão por semente in situ e na presença de uma mistura entre o emulsificante aniônico e a Pull como estabilizante.