Precipitation reaction in alpha-Cu-Al-Ag alloys

Precipitation reaction in alpha-Cu-Al-Ag alloys

Autor Silva, Ricardo Alexandre Galdino da Autor UNIFESP Google Scholar
Adorno, A.t. Google Scholar
Carvalho, T.m. Google Scholar
Magdalena, A.g. Google Scholar
Santos, C.m.a. Google Scholar
Instituição Universidade Federal de São Paulo (UNIFESP)
Universidade Estadual Paulista (UNESP)
Resumo The Ag-rich precipitates formation reaction in the Cu-9.22%at. Al-4.66%at. Ag, Cu-9.31%at. Al-5.83%at. Ag and Cu-9.37%at. Al-7.08%at. Ag alloys was studied using microhardness change measurements with temperature and time, differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The results indicated that the Ag-rich phase formation is an interface controlled process with a zero-order mechanism, due to the amount of unsolved Ag that makes the precipitation reaction rate independent of Ag concentration.
Palavra-chave Ag additions
Cu-based alloys
kinetics
Idioma Inglês
Financiador Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)
Data de publicação 2011-01-01
Publicado em Matéria (Rio de Janeiro). Rede Latino-Americana de Materiais, v. 16, n. 3, p. 747-753, 2011.
ISSN 1517-7076 (Sherpa/Romeo, fator de impacto)
Publicador Rede Latino-Americana de Materiais
Extensão 747-753
Fonte http://dx.doi.org/10.1590/S1517-70762011000300002
Direito de acesso Acesso aberto Open Access
Tipo Artigo
Web of Science WOS:000305880500002
SciELO S1517-70762011000300002 (estatísticas na SciELO)
Endereço permanente http://repositorio.unifesp.br/handle/11600/6240

Exibir registro completo




Arquivo

Nome: S1517-70762011000300002.pdf
Tamanho: 222.1KB
Formato: PDF
Descrição:
Abrir arquivo

Este item está nas seguintes coleções

Buscar


Navegar

Minha conta