Electrospinning TPU/poly o-phenetidine (POEA) fibers: influence of POEA on fiber morphology

Electrospinning TPU/poly o-phenetidine (POEA) fibers: influence of POEA on fiber morphology

Author Noronha Cruz, Karina Ferreira Autor UNIFESP Google Scholar
Botelho, Edson Cocchieri Google Scholar
Cristovan, Fernando Henrique Autor UNIFESP Google Scholar
Guerrini, Lilia Mueller Autor UNIFESP Google Scholar
Abstract The synthesis of poly (o-phenetidine) (POEA) was performed via chemical oxidative method and doped with dodecylbenzenesulfonic acid. Electrospun fibers of thermoplastic polyurethane (TPU)/poly o-phenetidine (POEA) blends were produced. Parameters such as the distance between collector and needle, as well as the applied voltage and the ratio of POEA content were evaluated. The fiber morphology, chemical structure and thermal analysis of the mats were analyzed. TPU nanofibers showed cylindrical morphology with many beads and the fiber diameter was around 330 nm. With the addition of POEA at a percentage of 30 wt% it was possible to produce uniform fibers without beads with diameters around 400 nm.
Keywords Poly o-phenetidine
Thermoplastic polyurethane
Polymer conductivity
xmlui.dri2xhtml.METS-1.0.item-coverage New York
Language English
Sponsor CNPq
Grant number CNPq: 2011/21694-5
FAPESP: 2011/21694-5
Date 2017
Published in Polymer Bulletin. New York, v. 74, n. 7, p. 2905-2919, 2017.
ISSN 0170-0839 (Sherpa/Romeo, impact factor)
Publisher Springer
Extent 2905-2919
Origin http://dx.doi.org/10.1007/s00289-016-1869-y
Type Article
Web of Science ID WOS:000403055600029
URI https://repositorio.unifesp.br/handle/11600/53630

Show full item record